Not only the isothermal oxidation behaviors at 900-1 300 ℃ for 20 h in air of bulk Ti3AlC2 with 2.8% TiC which was sintered by hot pressing with the additive of silicon,but also the cyclic oxidation behavior at 1 100-1 300 °C for 30 cycles,were investigated by using TG,XRD,SEM. The isothermal and cyclic oxidation behaviors generally follow a parabolic rate law. The parabolic rate constants of the former increased from 1.39×10-10 kg2/(m4·s) at 900 ℃ to 5.56×10-9 kg2/(m4·s) at 1 300 ℃. The calculated activation energy is 136.45 kJ/mol. The oxidation products are á-Al2O3 and little TiO2 at 900-1 000 ℃,however when the temperature is raised up to 1 200 ℃,TiO2 partially reacts to Al2TiO5,and the reaction is completed at 1 300 ℃. This demonstrates that Ti3AlC2 has excellent oxidation resistance and good thermal shock because the dense continuous oxide scale consists of mass á-Al2O3 and little TiO2 and/or Al2TiO5. Generally,the oxide scale is grown by the inward diffusion of O2- and the outward diffusion of Ti4+ and Al3+.