Corrosion Mechanism of MgO-CaO Brick for AOD Furnace

期刊名字：中國耐火材料（英文版）
文件大?。?/li>
論文作者：WANG Jiandong，GE Changchun，SHE
作者單位：School of Material Science and Engineering,Yingkou
更新時(shí)間：2023-02-27
下載次數(shù)：次

論文簡介

Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied. Results show that: The corrosion of MgOCaO brick is mainly attributed to the solution and infiltration of silicate liquid phase. Transverse cracks between reacted zone and original zone are parallel to the working face, which is an important factor for deteriorating the corrosion of MgO-CaO bricks.